5 results
Search Results
Now showing 1 - 5 of 5
Article Citation - WoS: 42Citation - Scopus: 42Sol-Gel Synthesis and Photocatalytic Activity of B and Zr Co-Doped Tio2(Pergamon-elsevier Science Ltd, 2013) Kapusuz, Derya; Park, Jongee; Ozturk, AbdullahEffects of boron (B) and/or zirconium (Zr) doping on photocatalytic activity of sol-gel derived titania (TiO2) powders were investigated. A conventional, non-hydrous sol-gel technique was applied to synthesize the B, Zr doped/co-doped TiO2 powders. Doping was made at molar ratios of Ti/B=1 and Ti/Zr=10. Sol-gel derived xero-gels were calcined at 500 degrees C for 3 h. The crystal chemistry and the morphology of the undoped and B, Zr doped/co-doped TiO2 nanoparticles were investigated using X-ray diffractometer and scanning electron microscope. Nano-scale (9-46 nm) TiO2 crystallites were obtained after calcination. Doping and co-doping decreased the crystallite size. Photocatalytic activity was measured through the degradation of methylene blue (MB) under 1 h UV-irradiation using a UV-vis spectrophotometer. Results revealed that B doping into anatase caused the formation of oxygen vacancies, whereas Zr addition caused Ti substitution. Both B and Zr ions had a profound effect on the particle morphology and photocatalytic activity of TiO2. The photocatalytic activity of B and Zr doped TiO2 particles increased from 27% to 77% and 57%, respectively. The best activity (88.5%) was achieved by co-doping. (C) 2013 Elsevier Ltd. All rights reserved.Article Citation - WoS: 47Citation - Scopus: 53Synthesis of Α-fe2o3< Heterogeneous Composites by the Sol-Gel Process and Their Photocatalytic Activity(Elsevier Science Sa, 2020) Bouziani, Asmae; Park, Jongee; Ozturk, Abdullahalpha-Fe2O3/TiO2 heterogeneous composites were synthesized by the sol-gel process to increase the photocatalytic activity of TiO2. The structural, morphological, and optical characteristics of the composites were determined by X-ray diffraction, scanning electron microscope, and UV-vis diffuse reflectance spectroscopy. Results revealed that the incorporation of alpha-Fe2O3 to TiO2 widened the visible light absorption ability of TiO2. It was realized that the calcination temperature plays a crucial role in morphology development hence photocatalytic activity of the alpha-Fe2O3/TiO2 heterogeneous composites. The photocatalytic activity of the composites calcined at various temperatures was evaluated for the degradation of Methylene Blue (MB) and Phenol (Ph) in aqueous medium under UV and sun-like illuminations. The alpha-Fe2O3-TiO2 composites exhibits superior photocatalytic efficiency to degrade both MB and Ph as compared to both pristine TiO2 and pristine alpha-Fe2O3 under sun-like illumination. The alpha-Fe2O3/TiO2 composite degraded approximately 90 % of MB and 50 % of Ph in 180 min sun-like illumination. Improvement in photocatalytic activity is attributed to the separation of photogenerated electron/hole pairs through the interaction of alpha-Fe(2)O(3 )and TiO2.Article Citation - WoS: 12Citation - Scopus: 11Enhanced Bioactivity and Low Temperature Degradation Resistance of Yttria Stabilized Zirconia/Clay Composites for Dental Applications(Elsevier Sci Ltd, 2022) Tufan, Yigithan; Park, Jongee; Ozturk, Abdullah; Ercan, BaturYttria stabilized zirconia (YSZ)/clay composites were produced to improve osseointegration and undesired tetragonal-to-monoclinic phase transformation (low temperature degradation, LTD) of YSZ ceramics so that long-term clinical success of YSZ implants is achieved. Various amounts (0.5,1,2, and 4 wt%) of clay was incorporated to YSZ. Predetermined amounts of clay and YSZ were mixed and pressed uniaxially at 15 MPa into compacts that were subsequently pressureless sintered at 1450 degrees C. Density, compressive strength, hardness and indentation crack resistance of 4 wt% clay incorporated YSZ/clay composite were 5.77 +/- 0.01 g/cm3, 1188 +/- 121 MPa, 1223 +/- 9 HV, and 4.4 +/- 0.1 MPa root m, respectively. Additionally, biological properties of YSZ/clay composites were assessed in vitro using bone cells. Incorporation of 4 wt% clay significantly enhanced bone cell prolifer-ation, spreading, and functions. Moreover, a significant increase in the LTD resistance of YSZ was achieved upon 4 wt% clay incorporation. The findings collectively suggest that YSZ/clay composites have a potential to be used as an alternative material for dental applications.Article Citation - WoS: 22Citation - Scopus: 25Facile synthesis of CsPbBr3/PbSe composite clusters(Taylor & Francis Ltd, 2018) Thang Phan Nguyen; Ozturk, Abdullah; Park, Jongee; Sohn, Woonbae; Tae Hyung Lee; Jang, Ho Won; Kim, Soo YoungIn this work, CsPbBr3 and PbSe nanocomposites were synthesized to protect perovskite material from self-enlargement during reaction. UV absorption and photoluminescence (PL) spectra indicate that the addition of Se into CsPbBr3 quantum dots modified the electronic structure of CsPbBr3, increasing the band gap from 2.38 to 2.48 eV as the Cs:Se ratio increased to 1:3. Thus, the emission color of CsPbBr3 perovskite quantum dots was modified from green to blue by increasing the Se ratio in composites. According to X-ray diffraction patterns, the structure of CsPbBr3 quantum dots changed from cubic to orthorhombic due to the introduction of PbSe at the surface. Transmission electron microscopy and X-ray photoemission spectroscopy confirmed that the atomic distribution in CsPbBr3/PbSe composite clusters is uniform and the composite materials were well formed. The PL intensity of a CsPbBr3/PbSe sample with a 1:1 Cs: Se ratio maintained 50% of its initial intensity after keeping the sample for 81 h in air, while the PL intensity of CsPbBr3 reduced to 20% of its initial intensity. Therefore, it is considered that low amounts of Se could improve the stability of CsPbBr3 quantum dots.Article Citation - WoS: 18Citation - Scopus: 19Synthesis and Enhanced Photocatalytic Activity of Nitrogen-Doped Triphasic Tio2 Nanoparticles(Elsevier Science Sa, 2019) Erdogan, Nursev; Bouziani, Asmae; Park, Jongee; Micusik, Matej; Kim, Soo Young; Majkova, Eva; Ozturk, AbdullahTiO2 nanoparticles of the single anatase phase, binary anatase-brookite phases, and ternary anatase-brookite-rutile phases were synthesized using an HNO3-catalyzed hydrothermal process. The types and amounts of phases varied depending on the hydrothermal synthesis conditions. The results revealed that N dissolves in different amounts and chemical states, depending on the phases present and their proportions in the nano particles. Brookite and rutile nanoparticles oriented through one direction were found to be crystallized by the surface transformation from anatase. Photocatalytic activity tests, evaluated by degradation of methylene blue (MB) under ultraviolet (UV) and visible light illumination, revealed that the N-doped TiO2 nanoparticles containing a ternary-phase mixture had the best photocatalytic activity. The MB degradation of the visible light-active nanoparticles was three times better than that of a commercially available well-known TiO2 powder, P25 under UV illumination. The enhanced photoactivity was attributed to the following: i) a high surface area, ii) suppression of the recombination of electron-hole pairs with ternary-phase mixture crystallized in heterojunctions, iii) larger anatase phase content, and iv) narrower band gap and facilitation of charge separation by dissolved N atoms.
