  • Thumbnail Image
    Article
    Citation - WoS: 22
    Antibacterial Performance of Pcl-Chitosan Core-Shell Scaffolds
    (Amer Scientific Publishers, 2018) Ozkan, Ozan; Sasmazel, Hilal Turkoglu
    In this study, antibacterial performance of the coaxially electrospun Poly-epsilon-caprolactone (PCL)-chitosan core-shell scaffolds developed, optimized and identified physically and chemically in our previous study, were evaluated for the suitability in wound healing applications. The aim of utilizing a core-shell fibrous scaffold with PCL as core and chitosan as shell was to combine natural biocompatibility, biodegradability and antibacterial properties of chitosan with mechanical properties and resistance to enzymatic degradation of PCL. The scaffolds were prepared with the optimized parameters, obtained from our previous study. Thickness and contact angle measurements as well as Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM) analyses confirmed repeated fabrication of PCL-chitosan core-shell scaffolds. In this study, assays specific to wound dressing materials, such as water vapor transmission rate (WVTR), in vitro degradability and antibacterial tests were carried out. WVTR value of PCL-chitosan core-shell scaffolds was higher (2315 +/- 3.4 g/m(2).day) compared to single PCL scaffolds (1654 +/- 3.2 g/m(2).day) due to the higher inter-fiber pore size. Additionally, in vitro degradability assays showed that the susceptibility of chitosan to enzymatic degradation can be significantly improved by hybridization with more resistant PCL while still keeping the scaffold to be considered as biodegradable. Finally, inhibition ratio and inhibition zone measurements showed that the PCL-chitosan core-shell polymeric scaffolds had significant antibacterial performance (52.860 +/- 2.298% and 49.333 +/- 0.719% inhibition ratios; 13.975 +/- 0.124 mm and 12.117 +/- 0.133 mm clear inhibition zones, against E. coli and S. aureus, respectively), close to the native chitosan. Therefore, the developed scaffolds can be considered as suitable candidates for biodegradable wound dressing applications.
  • Thumbnail Image
    Article
    Citation - WoS: 6
    Citation - Scopus: 7
    Hybrid Polymeric Scaffolds Prepared by Micro and Macro Approaches
    (Taylor & Francis As, 2017) Ozkan, Ozan; Sasmazel, Hilal Turkoglu
    Polymeric scaffolds with complex porous structures were fabricated with two different polymers by combining three fabrication methods in three steps, in which, nonwoven poly(e-caprolactone) microfibers were obtained with electrospinning and immersed in solvent cast chitosan solution poured in Petri dish to fabricate hybrid polymers, and finally the combined structure was freeze-dried with two different predrying techniques to obtain macropores in the structure. The resulting hybrid polymeric mats were found to have both microfibers and macroporosity due to the electrospinning as well as freeze-drying processes, which resemble the natural extracellular matrix. The optimized scaffolds that predried in the incubator at 40 degrees C for 5 h and then freeze-dried for 24 h exhibited contact angle value of 68.93 +/- 2.18 degrees with 3.252 +/- 0.783 MPa Young's modulus and 0.260 +/- 0.002 MPa yield strength as well as 1.35-fold cell yield in MRC5 fibroblast cell culture, compared to the commercial tissue culture polystyrene. [GRAPHICS] .