2 results
Search Results
Now showing 1 - 2 of 2
Article Citation - WoS: 44Citation - Scopus: 52Graphene-Supported Platinum Catalyst-Based Membrane Electrode Assembly for Pem Fuel Cell(Springer, 2016) Devrim, Yilser; Albostan, AyhanThe aim of this study is the preparation and characterization of a graphene-supported platinum (Pt) catalyst for proton exchange membrane fuel cell (PEMFC) applications. The graphene-supported Pt catalysts were prepared by chemical reduction of graphene and chloroplatinic acid (H2PtCl6) in ethylene glycol. X-ray powder diffraction, thermogravimetric analysis (TGA) and scanning electron microscopy have been used to analyze structure and surface morphology of the graphene-supported catalyst. The TGA results showed that the Pt loading of the graphene-supported catalyst was 31%. The proof of the Pt particles on the support surfaces was also verified by energy-dispersive x-ray spectroscopy analysis. The commercial carbon-supported catalyst and prepared Pt/graphene catalysts were used as both anode and cathode electrodes for PEMFC at ambient pressure and 70 degrees C. The maximum power density was obtained for the Pt/graphene-based membrane electrode assembly (MEA) with H-2/O-2 reactant gases as 0.925 W cm(2). The maximum current density of the Pt/graphene-based MEA can reach 1.267 and 0.43 A/cm(2) at 0.6 V with H-2/O-2 and H-2/air, respectively. The MEA prepared by the Pt/graphene catalyst shows good stability in long-term PEMFC durability tests. The PEMFC cell voltage was maintained at 0.6 V without apparent voltage drop when operated at 0.43 A/cm(2) constant current density and 70 degrees C for 400 h. As a result, PEMFC performance was found to be superlative for the graphene-supported Pt catalyst compared with the Pt/C commercial catalyst. The results indicate the graphene-supported Pt catalyst could be utilized as the electrocatalyst for PEMFC applications.Article Citation - WoS: 25Citation - Scopus: 25Preparation of Electrospun Pcl-Based Scaffolds by Mono/Multi-functionalized Go(Iop Publishing Ltd, 2019) Basar, Ahmet Ozan; Sadhu, Veera; Sasmazel, Hilal Turkoglu; Turkoglu Sasmazel, HilalIn the present study, sythetic biodegradable polymer poly(epsilon-caprolactone) (PCL) and graphene oxide (GO) were combined together to prepare 3D, composite tissue scaffolds (PCL/GO scaffolds) by using electrospinning technique. Also, the influence of Gly-Arg-Gly-Asp-Ser-Pro (GRGDSP) and/or thiophene (Th) modified GO on the composite PCL/GO mats (PCL/GO, PCL/GO-GRGDSP, PCL/ GO-Th, PCL/GO-GRGDSP-Th) was further investigated. Characteristic examinations of the scaffolds were carried out by scanning electron microscope (SEM), contact angle (CA) measurements, x-ray photoelectron spectroscopy, TGA, electrical conductivity tests, phosphate buffer saline absorption and shrinkage tests and mechanical tests. All of the scaffolds were exhibited suitable bead free and uniform morphology according to SEM images. With the addition of GO, better hydrophilicity and a slight CA decrease (similar to 5 degrees) for the PCL/GO scaffolds were observed. Mechanical properties were reinforced drastically with the addition and well-dispersion of GO into PCL matrix. The incorporation of PCL and GO exhibited enhanced electrical conductivity and the highest value was found for PCL/GO-GRGDSP-Th (2%) as 15.06 mu S cm(-1). The MG-63 osteoblast cell culture studies (MTT assay, ALP activity, Alizarin-Red staining, fluorescence and SEM analyses) showed that PCL/GO-GRGDSP-Th (1%) scaffolds exhibited the highest biocompatibility performance (1.87 fold MTT absorbance value comparing with neat PCL) due to the advanced properties of GO and the biological interfaces.
