4 results
Search Results
Now showing 1 - 4 of 4
Article Defect Characterization of Ga4se3< Layered Single Crystals by Thermoluminescence(indian Acad Sciences, 2016) Isik, M.; Delice, S.; Gasanly, N.Trapping centres in undoped Ga4Se3S single crystals grown by Bridgman method were characterized for the first time by thermoluminescence (TL) measurements carried out in the low-temperature range of 15-300 K. After illuminating the sample with blue light (similar to 470 nm) at 15 K, TL glow curve exhibited one peak around 74 K when measured with a heating rate of 0.4 K/s. The results of the various analysis methods were in good agreement about the presence of one trapping centre with an activation energy of 27 meV. Analysis of curve fitting method indicated that mixed order of kinetics dominates the trapping process. Heating rate dependence and distribution of the traps associated with the observed TL peak were also studied. The shift of peak maximum temperature from 74 to 113 K with increasing rate from 0.4 to 1.2 K/s was revealed. Distribution of traps was investigated using an experimental technique based on cleaning the centres giving emission at lower temperatures. Activation energies of the levels were observed to be increasing from 27 to 40 meV by rising the stopping temperature from 15 to 36 K.Article Citation - WoS: 9Citation - Scopus: 10A nonstandard numerical method for the modified KdV equation(indian Acad Sciences, 2017) Aydin, Ayhan; Koroglu, CananA linearly implicit nonstandard finite difference method is presented for the numerical solution of modified Korteweg-de Vries equation. Local truncation error of the scheme is discussed. Numerical examples are presented to test the efficiency and accuracy of the scheme.Article Citation - WoS: 12Citation - Scopus: 14Coating of Titanium Implants With Boron Nitride by Rf-Magnetron Sputtering(indian Acad Sciences, 2016) Gokmenoglu, Ceren; Ozmeric, Nurdan; Cakal, Gaye; Dokmetas, Nihan; Ergene, Cansu; Kaftanoglu, BilginSurface modification is necessary for titanium implants since it is unable to induce bone apposition. The beneficial effects of boron on bone formation, composition and physical properties make it suitable as a coating material. In the present study, surface properties of boron nitride (BN) coating on titanium implants were evaluated. Twenty-four implants and 12 abutments were coated with BN by RF-magnetron sputtering system. ATR-FTIR measurements were conducted to assess surface chemistry and morphology of BN-coated implants. Adhesion tests were performed by CSM nanoscratch test device to determine adhesion of BN to titanium surface. Surface profilometry and atomic force microscopy (AFM) was used to evaluate surface roughness. Mean roughness values were calculated. Contact angle measurements were done for evaluation of wettability. Surface characterization of coated implants was repeated after RF power of the system was increased and voltage values were changed to evaluate if these settings have an impact on coating quality. Three different voltage values were used for this purpose. Hexagonal-BN was determined in FTIR spectra. RF-coating technique provided adequate adherence of BN coatings to the titanium surface. A uniform BN coating layer was formed on the titanium implants with no deformation on the titanium surface. Similar roughness values were maintained after BN coating procedure. Before coating, the contact angles of the implants were in between 63(ay) and 79(ay), whereas BN coated implants' contact angles ranged between 46(ay) and 67(ay). BN-coated implant surfaces still have hydrophilic characteristics. The change in voltage values seemed to affect the surface coating characteristics. Especially, the phase of the BN coating was different when different voltages were used. According to our results, BN coating can be sufficiently performed on pretreated implant surfaces and the characteristics of BN coated surfaces can be changed with the change in parameters of RF-magnetron sputtering system.Article Citation - WoS: 64Citation - Scopus: 68On the Concept of Spectral Singularities(indian Acad Sciences, 2009) Guseinov, Gusein ShIn this paper, we discuss the concept of spectral singularities for non-Hermitian Hamiltonians. We exihibit spectral singularities of some well-known concrete Hamiltonians with complex-valued coefficients.