3 results
Search Results
Now showing 1 - 3 of 3
Article Citation - WoS: 8Citation - Scopus: 11Influence of the Heat Treatment on the Microstructure, Mechanical and High-Temperature Oxidation Behavior of Hastelloy X Alloy Fabricated Via Laser Powder Bed Fusion(Elsevier Science Sa, 2025) Ozer, Seren; Yalcin, Mustafa Alp; Bilgin, Gueney Mert; Davut, Kemal; Esen, Ziya; Dericioglu, Arcan F.The effect of building direction and heat treatment on the microstructure, mechanical properties, and high- temperature oxidation behavior of Hastelloy X (HX) alloy fabricated by the laser powder bed fusion (L-PBF) method was studied. Electron backscatter diffraction analyses revealed that the development of textured columnar grains with varying average grain sizes, boundary fractions, and dislocation densities induced the mechanical anisotropy observed in both horizontally and vertically fabricated samples. The yield strength (YS) values of the horizontally and vertically as-fabricated samples were determined as 605.7 +/- 15.9 MPa and 552.3 +/- 8.5 MPa, respectively. The post-processing heat treatment increased the ductility remarkably and reduced YS value down to similar to 445 MPa for all samples by the elimination of microstructural anisotropy and increased grain size subsequent to recrystallization. Oxidation tests conducted at 900 degrees C up to 100 h on as- fabricated samples exhibited severe intergranular oxidation, which was accompanied by the formation of large voids and microcracks as well as spallation of the oxide layer. In contrast, the heat-treatment improved the oxidation resistance of the alloy possibly due to the formation of uniform and dense Cr2O3 layer on the substrate surface.Article Citation - WoS: 1Citation - Scopus: 1Chemical Composition Optimization and Isothermal Transformation of Δ-Transformation Plasticity Steel for the Third-Generation Advanced High-Strength Steel Grade(Wiley-v C H verlag Gmbh, 2024) Okur, Onur; Davut, Kemal; Palumbo, Gianfranco; Nalcaci, Burak; Guglielmi, Pasquale; Yalcin, Mustafa Alp; Erdogan, MehmetA new low-manganese transformation-induced plasticity steel is designed with optimized nickel content to achieve superior strength and ductility while minimizing the use of expensive nickel. The steel is optimized using JMatPro software, then cast, and hot rolled. To assess the effect of intercritical annealing on austenite (martensite at room temperature) volume fraction and carbon content, hot-rolled steel samples quenched from different annealing temperatures (680-1100 degrees C) are used. Additionally, hot-rolled steel coupons are intercritically annealed at about 50% austenite formation temperature (740 degrees C) and then subjected to isothermal treatments at 300-425 degrees C for varying times (10-90 min). After optimizing these treatments to maximize retained austenite (RA), tensile specimens are heat-treated first at 740 degrees C and then isothermally at 325 degrees C. Thermodynamic calculations suggest that aluminum combined with silicon may lead to the delta ferrite formation, and even minimal nickel content can stabilize a considerable amount of austenite. In the experimental studies, it is shown that lower-temperature bainitic holding enhances austenite stability by enriching the carbon content. Optimized two-stage heat treatments yield up to 25.8% RA, with a tensile strength of 867.2 MPa and elongation of 40.6%, achieving a strength-elongation product of 35.2 GPax%, surpassing the third-generation advanced high-strength steel grades minimum requirement of 30 GPax%.Article Citation - WoS: 3Citation - Scopus: 3Nondestructive Microstructural Characterization of Austempered Ductile Iron(Walter de Gruyter Gmbh, 2023) Tuzun, Mert Yagiz; Yalcin, Mustafa Alp; Davut, Kemal; Kilicli, VolkanAustempered ductile iron (ADI) has been preferred in a wide range of applications due its unique combination of high strength, good ductility, wear resistance and fracture toughness together with lower cost and lower density compared to steels. Magnetic Barkhausen noise (MBN) measurement offers a better alternative to traditional characterization techniques by being fast and non-destructive. A simple linear regression using only one single independent variable cannot correlate the MBN with the microstructure of ADI, since its microstructure is multi component. Multiple linear regression analysis (MLRA) was used to build a model that uses the characteristic features of microstructural constituents as input parameters to predict the MBN. For that purpose, Cu-Ni-Mo alloyed ductile iron samples austempered between 325 and 400 degrees C and for 45-180 min duration were used. The results show that MBN is most sensitive to the size and shape of acicular ferrite and retained austenite. Moreover, MBN is almost insensitive to the size, morphology and volume fraction of graphite particles. This indicates that retained austenite pins the domain walls more effectively than the graphite particles. Considering the results MLRA, MBN technique can be used to characterize the ausferritic microstructure of ADI.
