Determination of Susceptibility To Intergranular Corrosion of Uns 31803 Type Duplex Stainless Steel by Electrochemical Reactivation Method: a Comparative Study
No Thumbnail Available
Date
2012
Journal Title
Journal ISSN
Volume Title
Publisher
Hindawi Ltd
Open Access Color
OpenAIRE Downloads
OpenAIRE Views
Abstract
In the present study as in our previous studies (Arikan and Doruk, 2008 and Arikan et al., 2012), similar specimens taken from a hot rolled cylindrical duplex stainless steel (DSS) bar with 22% Cr grade were solution annealed at 1050. C and then aged at 800. C from100 to 31622 min for sensitization treatment. Double loop electrochemical potentiodynamic reactivation and standard weight loss immersion acid tests were conducted. The solution annealed samples were found unsensitized. The samples aged for 100 min were less sensitized whereas samples aged for 316 min and more time were sensitized. The degree of sensitization (DOS) can be attributed to higher contribution of chromium and molybdenum depleted areas that result from intermetallic phases. However, especially the samples aged from 3162 to 31622 min have revealed chromium replenishment. Consequently, the degree of sensitization was lowered in comparison to the results obtained in previous studies.
Description
Doruk, Mustafa Çağrı/0009-0000-8238-2521
ORCID
Keywords
[No Keyword Available]
Turkish CoHE Thesis Center URL
Fields of Science
Citation
WoS Q
Scopus Q
Q2
Source
Volume
2012