Growth and Characterization of Inse/Ge Interfaces

Abstract

In the current study, we report the effect of insertion of a 200 nm thick Ge film between two layers of InSe. The Ge sandwiched InSe films are studied by means of X-ray diffraction technique, energy dispersion X-ray spectroscopy attached to a scanning electron microscope, optical spectrophotometry and light power dependent photoconductivity. It was observed that, The InSe prefers the growth of InSe monophase when deposited onto glass and the growth of gamma-In2Se3 when deposited onto InSe/Ge substrate. The three layers interface (InSe/Ge/gamma-In2Se3) exhibits a Ge induced crystallization process at annealing temperature of 200 degrees C. The optical analysis has shown that the InSe films exhibit a redshift upon Ge sandwiching. In addition, the conduction and valence bands offsets at the first interface (InSe/Ge) and at the second (Ge/gamma-In2Se3) interface are found to be 0.55 eV and 1.0 eV, and 0.40eVand 1.38 eV, respectively. Moreover, the photocurrent of the Ge sandwiched InSe exhibited higher photocurrent values as compared to those of InSe. On the other hand, the dielectric spectral analysis and modeling which lead to the identifying of the optical conduction parameters presented by the plasmon frequency, electron scattering time, free electron density and drift mobility have shown that the Ge sandwiching increased the drift mobility values from 10 cm(2)/Vs to 42 cm(2)/Vs. The main plasmon frequency also increased from 1.08 to 1.68 GHz. (C) 2017 Elsevier GmbH. All rights reserved.