Asidik pomza tozu ile katkılandırılmış akrilonitril-bütadien-stiren kompozitlerinin hazırlanması ve karakterizasyonu

Loading...
Thumbnail Image

Date

2017

Journal Title

Journal ISSN

Volume Title

Publisher

Open Access Color

OpenAIRE Downloads

OpenAIRE Views

Research Projects

Organizational Units

Organizational Unit
Chemical Engineering
(2010)
Established in 2010, and aiming to train the students with the capacity to meet the demands of the 21st Century, the Chemical Engineering Department provides a sound chemistry background through intense coursework and laboratory practices, along with fundamental courses such as Physics and Mathematics within the freshman and sophomore years, following preparatory English courses.In the final two years of the program, engineering courses are offered with laboratory practice and state-of-the-art simulation programs, combining theory with practice.

Journal Issue

Abstract

Akrilonitril-bütadien-stiren polimerinin fiziksel, termal ve reolojik özelliklerinin geliştirilmesi çalışmaları bu polimerin sahip olduğu geniş uygulama alnından dolayı halen ilgi çekmektedir. Bu çalışmada akrilonitril-bütadien-stiren matrisine asidik pomza tozu ilave edilerek kompozitler hazırlanmıştır. Kompozit hazırlama işlemi aynı yönde dönüş yapan çift vidalı mikrokarıştırıcı ile gerçekleştirilmiş ve test numuneleri enjeksiyon kalıplama ile elde edilmiştir. Asidik pomza parçacıklarının besleme oraları sırası ile %5, %10, %15 ve %20 olarak seçilmiştir. Hazırlanan kompozitlerin karaterizasyonları, çekme dayanımı testi, darbe testi erime akış indisi, dinamik mekanik analiz ve taramalı elektron mikroskobu ile yapılmıştır. Test sonuçlarına göre, kompozitler arasında en yüksek artış % 15 AP eklenmesi ile gözlenmiştir. Bu kompozisyon, ABS/AP kompozitleri için en uygun olarak belirlenmiştir.
The improvement of physical, thermal, rheological properties of acrylonitrile-butadiene-styrene polymers is still great interest of researches due to the large applications areas. In this work, acrylonitrile-butadiene-styrene matrix and acidic pumice particles were mixed in order to obtain composites. The composite preparations were achieved by using co-rotating twin-screw micro-compounder and the test specimens were obtained by injection-molding device. The feeding ratios of acidic pumice particles were chosen 5%, 10%, 15%, and 20% respectively. The characterizations of prepared composites were performed by tensile test, impact test, melt flow index measurement, dynamic mechanical analysis and scanning electron microscopy methods. According to test results, the maximum improvements were observed for 15% addition of AP among the composites. This composition was remarked as the most suitable for ABS/AP composites

Description

Keywords

Kimya Mühendisliği, Chemical Engineering, Polimer Bilim ve Teknolojisi, Polymer Science and Technology

Turkish CoHE Thesis Center URL

Fields of Science

Citation

WoS Q

Scopus Q

Source

Volume

Issue

Start Page

0

End Page

40