Development of Poly(vinyl Alcohol) (pva)/Reduced Graphene Oxide (rgo) Electrospun Mats
(Amer Scientific Publishers, 2019) Gozutok, Melike; Sadhu, Veera; Sasmazel, Hilal Turkoglu; Metallurgical and Materials Engineering
In this study, electrospun reduced graphene oxide (rGO) and poly(vinyl alcohol) (PVA) nanocomposites were developed with the concentration of rGO as 0.5 and 1.0 wt% by dispersing rGO in the PVA solution without using any co-solvent which may cause toxic effect for possible applications like packaging and tissue engineering. Water solubility of PVA was eliminated by UV-radiation crosslinking method. SEM analysis proved that continuous and bead-free nanofibers were obtained by electrospinning process and all electrospun mats had similar fiber characteristics with homogeneous fiber morphology. The average fiber diameter (nm), inter-fiber pore size (mu m) and the porosity (%) were increased with rGO incorporation. Additionally, enhanced tensile properties was achieved by rGO addition as the highest tensile strength was obtained as similar to 5 MPa for electrospun PVA+ 1.0 wt% rGO nanocomposites. ATR-FTIR analyses showed that there was a relatively strong interfacial interaction between rGO and PVA. Moreover, the thermal stability of obtained nanocomposites was enhanced by rGO addition without changing the crystal structure of PVA proved by XRD analyses. Also, improved electrical conductivity of the nanocomposites was obtained by rGO content as the highest conductivity (similar to 11 mu S.cm(-1)) was measured for electrospun PVA+ 1.0 wt% rGO.
Citation - WoS: 1
Citation - Scopus: 1
Physical and Biological Characteristics of Electrospun Poly (vinyl Alcohol) and Reduced Graphene Oxide Nanofibrous Structure
(Taylor & Francis Ltd, 2024) Sasmazel, Hilal Turkoglu; Alazzawi, Marwa; Gozutok, Melike; Sadhu, Veera; Metallurgical and Materials Engineering
The fabrication of graphene-based nanocomposites has been a topic of increasing interest due to graphene's exceptional physical properties and the ability to enhance the properties of various polymeric materials. Evaluating the biocompatibility of these nanocomposites is crucial to ensure their safe and effective use in biomedical applications. This study characterized and assessed the biocompatibility of previously fabricated electrospun polyvinyl alcohol (PVA)/reduced graphene oxide rGO fibrous structures by conducting a comprehensive assessment of their physical and biological characteristics. Contact angle measurements revealed that adding rGO to electrospun PVA fibers enhanced the surface wettability, improving the fibrous structure's PBS absorption capacity and degradation behavior. Including the rGO content resulted in a higher water vapor transmission rate, reaching similar to 48 g/m2day for PVA + 0.5 wt.% rGO and similar to 45 g/m2day for PVA + 1.0 wt.% rGO, compared to similar to 40 g/m2day for electrospun PVA fibers. Cell culture studies, including MTT assay, alkaline phosphatase (ALP) activity analysis, alizarin red staining, fluorescence microscopy, and SEM analyses, demonstrated that electrospun PVA + 1.0 wt.% rGO nanocomposites exhibited superior cell viability, proliferation, and growth compared to other samples, due to the improved physical properties of the PVA + 1.0 wt.% rGO fibrous structure.
Citation - WoS: 21
Citation - Scopus: 20
Preparation of Electrospun Pcl-Based Scaffolds by Mono/Multi-functionalized Go
(Iop Publishing Ltd, 2019) Basar, Ahmet Ozan; Sadhu, Veera; Sasmazel, Hilal Turkoglu; Metallurgical and Materials Engineering
In the present study, sythetic biodegradable polymer poly(epsilon-caprolactone) (PCL) and graphene oxide (GO) were combined together to prepare 3D, composite tissue scaffolds (PCL/GO scaffolds) by using electrospinning technique. Also, the influence of Gly-Arg-Gly-Asp-Ser-Pro (GRGDSP) and/or thiophene (Th) modified GO on the composite PCL/GO mats (PCL/GO, PCL/GO-GRGDSP, PCL/ GO-Th, PCL/GO-GRGDSP-Th) was further investigated. Characteristic examinations of the scaffolds were carried out by scanning electron microscope (SEM), contact angle (CA) measurements, x-ray photoelectron spectroscopy, TGA, electrical conductivity tests, phosphate buffer saline absorption and shrinkage tests and mechanical tests. All of the scaffolds were exhibited suitable bead free and uniform morphology according to SEM images. With the addition of GO, better hydrophilicity and a slight CA decrease (similar to 5 degrees) for the PCL/GO scaffolds were observed. Mechanical properties were reinforced drastically with the addition and well-dispersion of GO into PCL matrix. The incorporation of PCL and GO exhibited enhanced electrical conductivity and the highest value was found for PCL/GO-GRGDSP-Th (2%) as 15.06 mu S cm(-1). The MG-63 osteoblast cell culture studies (MTT assay, ALP activity, Alizarin-Red staining, fluorescence and SEM analyses) showed that PCL/GO-GRGDSP-Th (1%) scaffolds exhibited the highest biocompatibility performance (1.87 fold MTT absorbance value comparing with neat PCL) due to the advanced properties of GO and the biological interfaces.