Sajid, SajidAlzahmi, SalemWei, DongBen Salem, ImenPark, JongeeObaidat, Ihab M.Metallurgical and Materials Engineering2024-07-052024-07-05202312079-499110.3390/nano130202502-s2.0-85146770566https://doi.org/10.3390/nano13020250https://hdl.handle.net/20.500.14411/2481Sajid, Sajid/0000-0002-1165-1365; Park, Jongee/0000-0003-1415-6906; Ben Salem, Imen/0000-0002-3035-0402; Wei, Dong/0000-0002-6342-4658; Obaidat, Ihab M/0000-0002-7235-8998Simplifying device layout, particularly avoiding the complex fabrication steps and multiple high-temperature treatment requirements for electron-selective layers (ESLs) have made ESL-free perovskite solar cells (PSCs) attractive. However, the poor perovskite/substrate interface and inadequate quality of solution-processed perovskite thin films induce inefficient interfacial-charge extraction, limiting the power conversion efficiency (PCEs) of ESL-free PSCs. A highly compact and homogenous perovskite thin film with large grains was formed here by inserting an interfacial monolayer of diethanolamine (DEA) molecules between the perovskite and ITO substrate. In addition, the DEA created a favorable dipole layer at the interface of perovskite and ITO substrate by molecular adsorption, which suppressed charge recombination. Comparatively, PSCs based on DEA-treated ITO substrates delivered PCEs of up to 20.77%, one of the highest among ESL-free PSCs. Additionally, this technique successfully elongates the lifespan of ESL-free PSCs as 80% of the initial PCE was maintained after 550 h under AM 1.5 G irradiation at ambient temperature.eninfo:eu-repo/semantics/openAccessESL-free perovskite solar celldiethanolamineinterface modificationhigh performanceArticleQ1132WOS:00091634200000136678003