2024-07-182024-07-18https://hdl.handle.net/20.500.14411/6882The aim of this study is to improve the flame resistance and toughness of PLA by adding small amounts of different flame retardant additives and plasticizers at the same time. Poly(ethylene glycol) (PEG) was used as a plasticizer. Phosphate-based chemicals as flame retardant additives; ammonium polyphosphate (APP), boron phosphate (BP) and tri-phenyl phosphate (TPP) were used. Within the scope of the project, the synergistic effects of the double and triple compositions of these flame retardant additives were also examined. The mixtures are produced by melt blending and injection molding methods. The effect of the type and composition of flame retardant additives on the properties of PLA composites was determined by various mechanical, thermal and flammability tests.Bu çalışmanın amacı, PLA’nın alev dayanımını ve tokluğunu aynı anda, az miktarda farklı alev geciktirici katkı maddeleri ve plastikleştirici ekleyerek geliştirmektir. Plastikleştirici olarak poli(etilen glikol), (PEG) kullanılmıştır. Alev geciktirici katkı maddeleri olarak da fosfat bazlı kimyasallar; amonyum polifosfat (APP), bor fosfat (BP) ve tri-fenil fosfat (TPP) kullanılmıştır. Proje kapsamında bu alev geciktirici katkı maddelerinin ikili ve üçlü bileşimlerinin sinerjik etkileri de incelenmiştir. Karışımlar eriyikten harmanlama ve enjeksiyonla kalıplama yöntemleriyle üretilmiştir. Alev geciktirici katkı maddelerinin türünün ve bileşimlerinin PLA kompozitlerinin özelliklerine etkisi çeşitli mekanik, ısıl ve yanmazlık testleri ile belirlenmiştir.poly(lactic acid) (PLA), plasticizer, flame retardancypoli(laktik asit) (PLA), plastikleştirici, alev dayanımı