Güler, EnverSadeghi, SahlSanli, Lale IsikelGuler, EnverGursel, Selmiye AlkanChemical Engineering2024-07-052024-07-052018210167-27381872-768910.1016/j.ssi.2017.11.0172-s2.0-85037126117https://doi.org/10.1016/j.ssi.2017.11.017https://hdl.handle.net/20.500.14411/3023Gürsel, Selmiye Alkan/0000-0002-7966-6352; Güler, Enver/0000-0001-9175-0920We report here submicron-structured proton conducting poly(vinylidene fluoride)-graft-poly(styrene sulfonic acid) (PVDF-g-PSSA) membranes for polymer electrolyte membrane fuel cells (PEMFC). Highly conductive proton exchange membranes were obtained by single-step radiation grafting of sodium styrene sulfonate (SSS) to powder-form PVDF, followed by casting and subsequent solvent evaporation. The obtained submicron structure of membrane through solvent evaporation led to the arrangement of ionic channels proving increasing proton conductivity with the increase in graft level. In addition, a temperature above melting point of PVDF was used for solvent evaporation to allow melted PVDF to fill the formed pores, providing denser structure resulting in improved mechanical properties of the membranes. SSS grafting to PVDF powder was verified by NMR spectroscopy, and resultant membranes were characterized for proton conductivity, water up-take, morphology, mechanical and thermal properties, and fuel cell performance. According to preliminary tests, proton conductivities which were observed to increase with graft level were found to be around 70 mS cm(2) at 35% graft level. Thus, this led to a promising power density of 250 mW/cm(2) at 650 mA/cm(2).eninfo:eu-repo/semantics/closedAccessPEMFCMicrostructured membraneRadiation induced graftingArticleQ23146673WOS:000423889100011